300 Series Austenitic
|
| Type |
C |
Mn |
P |
S |
Si |
Cr |
Ni |
Mb |
|
| 302 |
0.15 |
2.00 |
0.045 |
0.030 |
1.00 |
17.00/19.00 |
8.00/10.00 |
- |
| 304 |
0.08 |
2.00 |
0.045 |
0.030 |
1.00 |
18.00/20.00 |
8.00/10.50 |
- |
| 304L |
0.03 |
2.00 |
0.045 |
0.030 |
1.00 |
18.00/20.00 |
8.00/12.00 |
- |
| 309 |
0.20 |
2.00 |
0.045 |
0.030 |
1.00 |
22.00/24.00 |
12.00/15.00 |
- |
|
| 309S |
0.08 |
2.00 |
0.045 |
- |
1.00 |
22.00/24.00 |
- |
- |
| 310 |
0.25 |
2.00 |
0.045 |
0.030 |
1.5 |
24.00/26.00 |
19.00/22.00 |
- |
| 310S |
0.08 |
2.00 |
0.045 |
0.030 |
1.5 |
24.00/26.00 |
19.00/22.00 |
- |
| 316 |
0.08 |
2.00 |
0.045 |
0.030 |
1.00 |
16.00/18.00 |
10.00/14.00 |
2.00/3.00 |
|
| 316L |
0.03 |
2.00 |
0.045 |
0.030 |
1.00 |
16.00/18.00 |
10.00/14.00 |
2.00/3.00 |
| 317 |
0.08 |
2.00 |
0.045 |
0.030 |
1.00/1.00 |
18.00/20.00 |
11.00/15.00 |
3.00/4.00 |
| 317L |
0.03 |
2.00 |
0.045 |
0.030 |
0.75 |
18.00/20.00 |
11.00/15.00 |
3.00/4.00 |
| 321 |
0.08 |
2.00 |
0.040 |
0.030 |
1.00 |
17.00/19.00 |
9.00/12.00 |
0.75/0.75 |
|
| 347 |
0.08 |
2.00 |
0.040 |
0.030 |
0.5/1.00 |
17.00/19.00 |
9.00/12.00 |
0.5/0.75 |
|
400 Series Martensitic
|
| Type |
C |
Mn |
P |
S |
N |
Si |
Cr |
Ni |
Mb |
|
| 410 |
0.15 |
1.00 |
0.040 |
0.030 |
- |
1.00 |
11.5 / 13.5 |
- |
- |
| 410S |
0.08 |
0.30/0.65 |
0.030 |
0.010 |
0.060 |
0.15/0.50 |
12.00 / 12.60 |
0.20/0.55 |
0.20/0.55 |
| 416 |
0.15 |
1.25 |
0.060 |
0.15 min |
- |
1.00 |
12.00 / 14.00 |
- |
- |
| 420 |
0.15 min |
1.00 |
0.040 |
0.030 |
- |
1.00 |
12.00 / 14.00 |
- |
- |
|
| 430 |
0.15 |
1.00 |
0.040 |
0.030 |
- |
1.00 |
16.00 / 18.00 |
- |
- |
| 440C |
0.95/1.20 |
1.00 |
0.040 |
0.030 |
- |
1.00 |
16.00 / 18.00 |
- |
0.75 |
|
Notes:
This table is intended for estimating purposes only and lists typical
chemical properties for a variety of 300 and 400 series stainless
steel grades. All values shown indicate the maximum percentage
unless otherwise noted. |
|